Pengaruh Waktu ElektroplatingCu-Mn Terhadap Laju Korosi Baja AISI 1020 Dalam Medium Korosif NaCl 3%

Ratna Noviyana, Ediman Ginting Suka, Yayat Iman Supriyatna

Abstract


The influence of electroplating time Cu-Mn to corrosion rate of Steel AISI 1020 in corrosive medium NaCl 3% had been researched. Corrosion rate testing is used weight loss method by soaking the samples in the corrosive medium NaCl for 168 hours. The results showed that the longer time electroplating that used, the corrosion rate will be decreased. This is because the growing number of Cu and Mn ions deposited on the surface of the sample after electroplating. The lowest corrosion rate obtained at the time of 50 seconds that is 0.098 mmpy. The analysis results of metallurgical microscope showed that the coating looks thicker with increasing time of electroplating, while after corrosion rate tested thecoatings being black and a few coating of samples were cracked due to corrosion.The X-Ray Diffraction (XRD) characterization result showed thatthe phase of AISI 1020 raw material after corrosion tested is changed from pure iron (Fe) to magnetite phase (Fe3O4).

Keywords


Steel AISI 1020, electroplating Cu-Mn, NaCl 3%

Full Text:

PDF

References


E. Budiyanto, D. A. Setiawan, H. Supriadi, and Ridhuan, “Pengaruh Jarak Anoda-Katoda Pada Proses Elektroplating Tembaga Terhadap Ketebalan Lapisan dan Efisiensi Katoda Baja AISI 1020,” J. TURBO, vol. 5, no. 1, 2016.

F. Afriani, Komalasari, and Zultiniar, “Proteksi Katodik Metode Anoda Tumbal untuk Mengendalikan Laju Korosi,” J. FTEKNIK, vol. 1, no. 2, pp. 1–12, 2014.

A. Radisic, J. L. Hernandez, G. Tokei, G. P. Beyer, and P. M. Vereecken, “Electrochemical Deposition of Manganese and Copper Manganese Alloy on Silicon,” Electrochem. Soc., vol. 3, no. 21, pp. 69–76, 2007.

Z. I. Ortiz, P. Díaz-Arista, Y. Meas, R. Ortega-Borges, and G. Trejo, “Characterization of the Corrosion Products of Electrodeposited Zn, Zn-Co and Zn-Mn Alloys Coatings,” Corros. Sci., vol. 51, no. 11, pp. 2703–2715, 2009.

P. Díaz-Arista, Z. I. Ortiz, H. Ruiz, R. Ortega, Y. Meas, and G. Trejo, “Electrodeposition and characterization of Zn-Mn alloy coatings obtained from a chloride-based acidic bath containing ammonium thiocyanate as an additive,” Surf. Coatings Technol., vol. 203, no. 9, pp. 1167–1175, 2009.

A. M. Chockalingam, U. R. K. Lagudu, and S. V. Babu, “Potassium Periodate-Based Solutions for Minimizing Galvanic Corrosion at the Cu-Mn Interface and for Polishing the Associated Cu Interconnect Structures,” ECS J. Solid State Sci. Technol., vol. 2, no. 4, pp. 160–165, 2013.

ASTM Internaional, Standard Practice for Laboratory Immersion Corrosion Testing of Metals 1. United States, 2004.

Y. D. Mustopo, Pengaruh Waktu terhadap Ketebalan dan Adhesivitas Lapisan pada Proses Elektroplating Krom Dekoratif tanpa Lapisan Dasar, Dengan Lapisan Dasar Tembaga dan Tembaga-Nikel. Surakarta: Universitas Sebelas Maret, 2011.

W. E. Triastuti and A. Subekti, “Karakter Fisik dan Korosi Mangan Hasil Pelapisan pada Baja AISI 1020,” J. KAPAL, vol. 9, no. 1, pp. 1–7, 2013.

W. E. Triastuti and D. B. P, “Efek Penambahan Ion Tartrate Terhadap Elektrodeposisi Mn-Cu Pada Pipa Baja Karbon,” J. KAPAL, vol. 9, no. 3, pp. 167–170, 2012.




DOI: http://dx.doi.org/10.23960%2Fjtaf.v5i2.1817

This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.