Pengaruh waktu milling terhadap Sifat mikro struktur dan magnet dari NdFeB dengan proses Wet dan Dry milling

Wahyu Solafide Sipahutar, William Wiliiam, Muljadi Muljadi

Abstract


Making of magnets from NdFeB flakes by Wet and dry milling to determine the microstructure, physical and magnetic properties of the milling time variation is 16, 24, and 48 hours. The milling powder is then analysed to determine the particle size with PSA and XRD to determine the phase formed. Then the compacting process with isotropy printing for making pellet test samples with a pressure of 7 tons for 2 minutes. Then the pellet sample, given annealing temperature with a variation of 150 and 170 ̊C, then a measurement of magnetic properties with a Gauss Meter. The results obtained by the smallest optimum particle size with 48 hours of milling time at a diameter of 90% 4.7 μm, while the results of dry milling at a diameter of 90% amounted to 60.85 μm. The best method to get the smallest particle size is the Wet milling method. XRD results with Wet and Dry milling phases that appear only Nd2Fe14B phase. As milling time increases, the resulting density increases. The largest magnetic flux testing with dry milling method with 48 hours of milling time for temperatures 170 ̊C temperature obtained 468.5 Gauss and the addition of annealing temperature the magnetic properties of the material is getting better.


Keywords


Dry milling, Fluks Magnetic,Microstructure, NdFeB, Wet milling

Article Metrics

Abstract view : 108 times
PDF - 124 times

Full Text:

PDF

References


M. Hilda Ayu, Syahrul Humaidi, “Pengaruh Komposisi Poliester Terhadap Sifat Magnet Dan Mekanik Pada Pembuatan Bonded Magnet Pr-Fe-B,” USU, 2013.

and C. O. D.W.Scott, M. Ma, Y. L. Liang, “Bounds, Microstructural control of NdFeB castingots for achieving 50 MGOe sintered magnets,” J. Appl. Phys., vol. 79, no. 8, pp. 4830–4832, 1996.

J. Fraden, Handbook of Modern Sensors: Physics, Design, and Applications. Springer US, 2010.

E. dan M. Yuliati, “Penghalusan Serbuk dan Efeknya Pada Fasa dan Sifat Magnetik Sistem Magnet Permanen Berbasis Nd2Fe14B,” J. Sains Mater. Indones., vol. 7, no. 1, pp. 21–24, 2005.

P. M. Sardjono, “Analisis Struktur Kristal dan Mikrostruktur Serbuk Nd2Fe14B Hasil Proses Mechanical Alloying,” in Prosiding Pertemuan Ilmiah XXVIII HFI Jateng & DIY, 2013, pp. 29–34.

T. R. S. William, “Pengaruh Waktu Dry Milling Terhadap Karakteristik Dan Sifat Magnet Permanen Nd-Fe-B.,” J. Fis. dan Apl., vol. 1, no. 1, 2016.

W. Solafide, “Efek Waktu Wet Milling Dan Suhu Annealing Terhadap Sifat Fisis, Mikrostruktur Dan Magnet Dari Flakes Ndfeb,” 2015.

W. Sipahutar, “Efek Waktu Wet Milling dan Suhu Annealing Terhadap Sifat Fisis, Mikrostruktur dan Magnet dari Flakes NdFeB,” USU, 2015.

A. Fiandimas, A. dan Manaf, “Pembuatan Magnet Permanen Barium Heksaferit Berbahan Baku Mill Scale dengan Teknik Metalurgi Serbuk,” J. Sains Mater. Indones., vol. 5, pp. 5–50, 2003.

T. P. Radyumikono, Nofrizal, Dwiwahyu Nugroho, “Sintesis Nano-partikel Zno Dengan Metode Mechano-chemical Milling,” in Prosiding Pertemuan Ilmiah Ilmu Pengetahuan dan Teknologi Bahan, 2012, pp. 60–62.

E. H. Wahyuni, M.S., “Karakterisasi Cangkang Kerang Menggunakan XRD dan X-Ray Physics Basic Unit,” J. Neutrino, vol. 3, pp. 34–38, 2010.

S. P. R. Mujamillah, Bambang S., Evy Y., M.Refai M., “Sifat Magnetik Bahan Komposit Berbasis Serbuk Magnet NdFeB Hasil Milling dan Polimer Termoplastik LLDPE,” J. Sains Mater. Indones., vol. 3, pp. 6–9, 2002.

Suharpiyu, “Pengaruh Komposlsl Dan Beban Tekan Terhadap Rarakteristik Rigid Bonded Magnet Berbasis Logam Tanah Jarang Nd-Fe-B Dengan Bahan Pengikat Resin Poliester,” 2000.

R. Akmal Johan, “Magnetik Nanokristalin Barium Heksaferit (BaO6Fe2O3) Hasil Proses High Energy Milling,” J. Sains Mater. Indones., pp. 120–125, 2007.




DOI: http://dx.doi.org/10.23960%2Fjtaf.v9i1.2695

This work is licensed under a This work is licensed under a Creative Commons Attribution 4.0 International License.