Material Absorber Gelombang Elektromagnetik Berbasis (La0.8Ba0.2)(Mn(1-x)/2ZnxFe(1-x)/2)O3(x = 0 – 0,6)

Intan Wandira, Pulung Karo Karo, Wisnu Ari Adi

Abstract


Electromagnetic wave absorber materials with(La0.8Ba0.2)(Mn(1-x)/2ZnxFe(1-x)/2)O3(x = 0-0,6) had been researched. This magnetic material was synthesized by using solid state reaction method and a suitable composition for the application of a microwave absorber material had been obtained, namely (La0.8Ba0.2)(Mn0.4Zn0.2Fe0.4)O3 (x = 0,2).Precursors use wereLa2O3, BaCO3, ZnO, Fe2O3, dan MnCO3. The mixture was mixed with High Energy Milling for 5 hours then sintered at 1000 ° C for 5 hours.The result of refinement of X-ray diffraction pattern shows that (La0.8Ba0.2)(Mn0.4Zn0.2Fe0.4)O3material had a single phase and a trigonal structure. The surface morphology of the sample had a uniform spherical shape. The results of absorbance analysis of samples to electromagnetic waves in the range of 8-12 GHz was 96%. Thus, the (La0.8Ba0.2)(Mn0.4Zn0.2Fe0.4)O3 (x = 0,2) material was a potential candidate for applications of electromagnetic wave absorber material.

Keywords


absorber,phase, perovskite (La0.8Ba0.2)(Mn(1-x)/2ZnxFe(1-x)/2)O3, solid state reaction

Article Metrics

Abstract view : 863 times
PDF - 935 times

Full Text:

PDF

References


Y. J. An, K. Nishida, T. Yamamoto, S. Ueda, and T. Deguchi, “Characteristic evaluations of microwave absorbers using dielectric and magnetic composite materials,” vol. 9, no. 4, pp. 430–436, 2008.

I. Subiyanto, “Universitas Indonesia Perhitungan Impedansi pada bahan La 0.67 Sr 0.33 Mn,” 2011.

H. Zhang, X. Yao, M. Wu, L. Zhang, H. Zhang, X. Yao, M. Wu, and L. Zhang, “Complex permittivity andpermeability of Zn – Co substituted Z type hexaferrite prepared by citrate sol – gel process Complex permittivity and permeability of Zn – Co substituted Z type hexaferrite prepared by citrate sol – gel process,” vol. 102, no. 1, pp. 9–15, 2016.

W. A. A. Sebayang, Perdamean, Muljadi, “Analisis Struktur Kristal SrO . 6Fe2O3 Menggunakan Program General Structure Analysis System Dan Pengujian Sifat Magnetnya,” vol. 12, no. 3, pp. 55–62, 2011.

S. Sugiantoro and A. Adi, “Karakterisasi Termal Bahan Magnetik Sistem,” vol. 3, no. 1411–2213, pp. 3–6, 2012.

K. Zhou, H. Xia, K. Huang, L. Deng, D. Wang, Y. Zhou, and S. Gao, “The microwave absorption properties of La 0 . 8 Sr 0 . 2 Mn 1 À y Fe y O 3 nanocrystalline powders in the frequency range 2 – 18 GHz,” vol. 404, no. 2, pp. 175–179, 2009.

P. Sardjono and W. A. Adi, “Structural , Magnetic and Electrical Properties of La 1-x Ba x MnO 3 ( x = 0 – 0 . 7 ) for Absorber Electromagnetic Wave,” vol. 3, no. 7, pp. 230–234, 2013.

B. H. Toby, “R Factors in Rietveld Analysis : How Good is Good Enough,” vol. 21, no. March 2006, pp. 67–70, 2014.




DOI: http://dx.doi.org/10.23960%2Fjtaf.v6i1.1827