Pengaruh Variasi Konsentrasi HCl Pada Pembentukan Nanosilika Berbasis Batu Apung

Lusi Vusfita Sari, Posman Manurung, Yanti Yulianti

Abstract


The aims of this research is to determine the effect of variation concentration of HCl on chemical composition, phase formed, and particle size on pumice powder. Nanosilica is made using the solgel method with NaOH concentration 4 M, H2SO4 5 M and variation concentration of HCl 0,5; 0,75; 1; 1,25 dan 1,5 M. The XRF results showed the greatest chemical composition value in the silica pumice powder sample with a value of 77.80%. This value is higher after synthesis at the highest chemical composition value in the nanosilica sample 1,25 M HCl concentration of 87.05%. The XRD results show a diffractogram of pumice powder samples formed by anorthite and albite phases while in the nanosilica sample 1,25 M HCl concentrates are debated with the amorphous phase. The TEM results show particle size of nanosilic sample 1,25 M HCl concentration is 5 nm with average particle size (12.02 ± 3.23) nm.

Keywords


Nanosilica, pumice, leaching, HCl, solgel

Full Text:

PDF

References


C. H. E. Stehn, “Krakatau,” Netherlands East Indie Volcanol. Surv., pp. 44–48, 1932.

M. Halim and S. Arsalane, “The Synthesis and Characterization of Low-cost Mesoporous Silica SiO 2 from Local Pumice Rock Regular Paper,” 2015.

K. Srivastava, N. Shringi, V. Devra, and A. Rani, “Pure Silica Extraction from Perlite : Its Characterization and Affecting factors,” vol. 2, no. 7, pp. 2936–2942, 2013.

B. R. Fernandez, “Sintesis nanopartikel SiO2 menggunakan metode sol-gel dan aplikasinya terhadap aktifitas sitotoksik sel,” J. Nanoteknologi, vol. 3, no. 2, pp. 384–389, 2012.

S. dan A. Mukunda, H, “A novel process and apparatus for the manufacturer of precipitated silica from rice hull,” Int. Apllication Publ. under Pat. Coop. Treaty WO, 2004.

A. Coniwanti P. dan S. Rasmiah, “Pengaruh proses pengeringan, normalitas HCl, dan temperatur pembakaran pada pembuatan silika Dari sekam padi,” J. Tek. Kim., vol. 1, no. 15, pp. 5–11, 2008.

Azhari dan Muchtar Aziz, “Sintesis dan karakterisasi material berpori berbasis mineral silika pulau belitung,” J. Teknol. Miner. Dan Batubara, vol. 12, no. 3, pp. 161 – 170, 2016.

P. Galliker, P., Hommes, G. Schlasser, D., Corvini, P. F. X. dan Shahgaldin, “Laccase modified silica nanoparticles efficiently catalyze the transformation of phenolic compounds,” J. Colloid Interface Sci., vol. 349, pp. 99–105, 2010.

H. H. Liu, V. H., Thuc, C. N., Thuc, “Synthesis of silica nanoparticles from vietnamese rise husk by solgel method,” J. Powder Technol., pp. 1–10, 2013.

C. Latif, “Pengaruh Variasi Temperatur Kalsinasi Pada Struktur Silika,” vol. 3, no. 1, pp. 4–7, 2014.

B. Adjiantoro and E. Mabruri, “Proses pemurnian silikon tingkat metalurgi dengan menggunakan metoda pelarutan kimia.,” Maj. Metal., vol. 25, no. 2, pp. 71–78, 2010.

Samin dan Susanna, “Kajian Adsorpsi Cr3+ pada Breksi Batu Apung Wukirsari,” Pros. Pertem. dan Present. Ilm. Penelit. Dasar Ilmu Pengetah. dan Teknol., pp. 56–63, 2002.

S. Miskah, “Pemanfaatan batu apung (pumice) sebagai bahan pemucat crude palm oil,” J. Tek. Kim., vol. 17, no. 2, p. 3, 2010.

Nuryono, “Pengaruh konsentrasi NaOH pada peleburan abu sekam padi cara basah,” Pros. Semin. Nas. Has. Penelit. FMIPA. UNDIP, 2004.

A. Zukira, Paputungan, M. dan Musa, W, J, “Analisis Logam -Logam pada Batu Apung dan Modifikasinya Serta Uji Adsorpsinya pada Larutan Asam Asetat,” J. Sainstek, vol. 6, pp. 462–557, 2012.

A. Sarikaya, M., Depci, T., Aydogmus, R., dan Yucel, “Production of nano amorphous SiO2 from malatya pyrophyllite,” J. Earth Environ. Sci., vol. 44, pp. 295–305, 2016.

S. N. G. Bakar dan R. A., Rosiyah Y., “Production of high purity amorphous silica from rice husk,” J. Procedia Chem., vol. 19, pp. 189 – 195, 2016.




DOI: http://dx.doi.org/10.23960%2Fjtaf.v7i2.1945

This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.