Pengaruh Temperatur Austenisasi terhadap Struktur Mikro dan Nilai Kekerasan Material 14%Cr-3%Ni-2%Mo-2%C untuk Aplikasi Bola Gerus

Imaniar Romaeni, Posman Manurung, Fajar Nurjaman

Abstract


This study was conducted to determine the effect of heat treatment in the form of sub-critical, austenization, quenching and tempering the hardness values of the white cast iron material as consideration for testing wear resistance of local and foreign products as grinding balls. Samples was treated sub-critical at a temperature of 700°C with a hold time of 2 hours and continued with austenization temperature variation of 850, 950 and 1050°C with a hold time of each sample is 5 hours. The optimum hardness value was obtained at a temperature of 950°C austenization in the amount of 68.3 HRC and decreased at a temperature of 1050°C. It is because the solubility of carbon elements making up the matrix. Next will be tempering at a temperature of 250°C and holding time 2 hours hardness values decreased but the value of wear resistance is obtained even better ie grinding balls of 0.03 g/kg of product due to the combination of its constituent elements, namely chromium-molybdenum and nickel are high the presence of wear phenomena induced martensite.

Keywords


imaniarromaeni@gmail.com

Article Metrics

Abstract view : 361 times
PDF - 87 times

Full Text:

PDF

References


P. Ortega-Cubillos, P. A. Nannetti-Bernardini, M. Celso-Fredel, and R. A. Campos, “Wear resistance of high chromium white cast iron for coal grinding rolls,” Rev. Fac. Ing., 2015.

Y. Matsubara, N. Sasaguri, K. Shimizu, and S. Kon Yu, “Solidification and abrasion wear of white cast irons alloyed with 20% carbide forming elements,” Wear, 2001.

Ratna Kartikasari, R Soekrisno, and M Noer Ilman, “Karakterisasi Ball Mill Import pada Industri Semen di Indonesia,” J. Tek. Mesin, 2007.

N. I. Nasir, “Effect of Heat Treatment On The Mechanical Properties of Stainless Steel Type 304,” Inter-national J. Scrientific Eng. Res., vol. 3, pp. 87–93, 2015.

T. V Rajan, C. P. Sharma, and A. Sharma, Heat Treatment: Principles and Techniques. New Delhi: Prentice-Hall of India, 1994.

A. E. Karantzalis, A. Lekatou, and H. Mavros, “Microstructural Modifications of As-Cast High-Chromium White Iron by Heat Treatment,” J. Mater. Eng. Perform., 2009.

D. Kopycinski, E. Guzik, D. Siekaniec, and A. Szczesny, “Analysis of the high chromium cast iron microstructure after the heat treatment,” Arch. Foundry Eng., 2014.

F. Nurjaman, W. Riansyah, and B. Suharno, “Pengaruh Temperatur Auste-nisasi terhadap Karakteristik High Chromium White Cast Iron Dengan Perlakuan Sub-Zero (Cryogenic),” Pros. Semin. Ilmu Penge-tahuan Tek., vol. 2, pp. 65–70, 2012.

F. Nurjaman, B. Suharno, W. Astuti, and M. Aryati, “Karakteristik Grinding Ball Impor Asal India dan China,” Pros. SENAMM, vol. V, pp. 78–84, 2012.

A. Wiengmoon, J. T. H. Pearce, and T. Chairuangsri, “Relationship between microstructure, hardness and corrosion resistance in 20 wt.%Cr, 27 wt.%Cr and 36 wt.%Cr high chromium cast irons,” Mater. Chem. Phys., 2011.

A. Sinatora, M. Pohl, and E. U. Waldherr, “Wear Induced Martensite In High Chromium Cast Iron,” Scr. Metall. Mater., vol. 32, no. 6, pp. 857–861, 1995.




DOI: http://dx.doi.org/10.23960%2Fjtaf.v5i2.1381

This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.